Abstract Based on the three-stage fatigue crack growth pica limon packets model, a corrosion fatigue life prediction method considering the coupling effect of corrosion and fatigue is proposed in this paper.In this case, stress factor amplitude was claimed considering the coupling effect of corrosion and fatigue.Three push-out tests in corrosion conditions were conducted to study the failure mode of studs.
The crack propagation of studs, obtained through the daddario ej10 push-out tests, was simulated in FRANC 3D to establish a library of adequate stress factor amplitude.According to the corrosion degree of the specimens, the corrosion dissolution rate formula was formed, and the corrosion fatigue life of the specimen was predicted.Results show that the error between the predicted and experimental values is approximately 25%.